Semiconductor Device, Tool, and Method of Manufacturing

ABSTRACT

A semiconductor device is manufactured using a cleaning process. The cleaning process utilizes a semiconductor manufacturing tool that has a wet cleaning section and a plasma cleaning section. The semiconductor device is placed within a wet cleaning chamber within the wet cleaning section, where a wet cleaning process is performed. Once completed, and without breaking atmosphere, the semiconductor device is removed from the wet cleaning section and placed within a plasma cleaning chamber within the plasma cleaning section. A plasma clean is then performed.

PRIORITY CLAIM AND CROSS-REFERENCE

This application is a divisional of U.S. application Ser. No.15/666,063, filed on Aug. 1, 2017, which claims priority to and thebenefit of U.S. Provisional Application No. 62/512,909, filed on May 31,2017, entitled “Semiconductor Device, Tool, and Method ofManufacturing,” which applications are hereby incorporated herein byreference in their entireties.

BACKGROUND

Semiconductor devices are used in a variety of electronic applications,such as, for example, personal computers, cell phones, digital cameras,and other electronic equipment. Semiconductor devices are typicallyfabricated by sequentially depositing insulating or dielectric layers,conductive layers, and semiconductor layers of material over asemiconductor substrate, and patterning the various material layersusing lithography and etching processes to form circuit components andelements thereon.

The semiconductor industry continues to improve the integration densityof various electronic components (e.g., transistors, diodes, resistors,capacitors, etc.) by continual reductions in minimum feature size, whichallow more components to be integrated into a given area. However, asthe minimum features sizes are reduced, additional problems arise withineach of the processes that are used, and these additional problemsshould be addressed.

BRIEF DESCRIPTION OF THE DRAWINGS

Aspects of the present disclosure are best understood from the followingdetailed description when read with the accompanying figures. It isnoted that, in accordance with the standard practice in the industry,various features are not drawn to scale. In fact, the dimensions of thevarious features may be arbitrarily increased or reduced for clarity ofdiscussion.

FIGS. 1A-1C illustrate formation of a via opening and a trench openingin a low k dielectric, in accordance with some embodiments.

FIGS. 2A-2C illustrate a semiconductor manufacturing tool, in accordancewith some embodiments.

FIG. 3 illustrates formation of conductive material within the viaopening and the trench opening in accordance with some embodiments.

DETAILED DESCRIPTION

The following disclosure provides many different embodiments, orexamples, for implementing different features of the invention. Specificexamples of components and arrangements are described below to simplifythe present disclosure. These are, of course, merely examples and arenot intended to be limiting. For example, the formation of a firstfeature over or on a second feature in the description that follows mayinclude embodiments in which the first and second features are formed indirect contact, and may also include embodiments in which additionalfeatures may be formed between the first and second features, such thatthe first and second features may not be in direct contact. In addition,the present disclosure may repeat reference numerals and/or letters inthe various examples. This repetition is for the purpose of simplicityand clarity and does not in itself dictate a relationship between thevarious embodiments and/or configurations discussed.

Further, spatially relative terms, such as “beneath,” “below,” “lower,”“above,” “upper” and the like, may be used herein for ease ofdescription to describe one element or feature's relationship to anotherelement(s) or feature(s) as illustrated in the figures. The spatiallyrelative terms are intended to encompass different orientations of thedevice in use or operation in addition to the orientation depicted inthe figures. The apparatus may be otherwise oriented (rotated 90 degreesor at other orientations) and the spatially relative descriptors usedherein may likewise be interpreted accordingly.

Embodiments will now be described with respect to particularembodiments, such as a cleaning process during a via first, trench lastdamascene process for a 20 nm, 16 nm, 10 nm, 7 nm, or 5 nm process node.However, the ideas described herein can applied in any suitable process.

With reference now to FIGS. 1A-1C, FIG. 1A illustrates a substrate 101with active devices (not separately illustrated), metallization layers103 (including both an unlabeled dielectric material and conductiveelements 105 within the dielectric material), a first etch stop layer107, a second etch stop layer 109, a third etch stop layer 110, and afirst dielectric layer 111. In an embodiment the substrate 101 maycomprise bulk silicon, doped or undoped, or an active layer of asilicon-on-insulator (SOI) substrate. Generally, an SOI substratecomprises a layer of a semiconductor material such as silicon,germanium, silicon germanium, SOI, silicon germanium on insulator(SGOI), or combinations thereof. Other substrates that may be usedinclude multi-layered substrates, gradient substrates, or hybridorientation substrates.

The active devices may comprise a wide variety of active devices such astransistors and the like and passive devices such as capacitors,resistors, inductors and the like that may be used to generate thedesired structural and functional parts of the design. The activedevices and passive devices may be formed using any suitable methodseither within or else on the substrate 101.

The metallization layers 103 are formed over the substrate 101 and theactive devices and are designed to connect the various active devices toform functional circuitry for the design. In an embodiment themetallization layers are formed of alternating layers of dielectric andconductive material and may be formed through any suitable process (suchas deposition, damascene, dual damascene, etc.). In an embodiment theremay be one to four layers of metallization separated from the substrate101 by at least one interlayer dielectric layer (ILD), but the precisenumber of metallization layers is dependent upon the design.

The conductive elements 105 may be formed in an upper portion of themetallization layers 103, and is a region to which an interconnect 305(not illustrated in FIG. 1A but illustrated and described below withrespect to FIG. 3) will make physical and electrical connection. In anembodiment the conductive elements 105 may be a material such as copperformed using, e.g., a damascene or dual damascene process, whereby anopening is formed within an upper portion of the metallization layers103, the opening is filled and/or overfilled with a conductive materialsuch as copper, and a planarization process is performed to embed theconductive material within the metallization layers 103. However, anysuitable material and any suitable process may be used to form theconductive elements 105.

A first etch stop layer 107 is used to protect the underlying structuresand provide a control point for a subsequent etching process through,e.g., the second etch stop layer 109. In one embodiment, the first etchstop layer 107 may be formed of aluminum oxynitride (AlON) using plasmaenhanced chemical vapor deposition (PECVD), although other materialssuch as nitrides, carbides, borides, combinations thereof, or the like,and alternative techniques of forming the first etch stop layer 107,such as low pressure CVD (LPCVD), PVD, or the like, could alternativelybe used. The first etch stop layer 107 may have a thickness of betweenabout 50 Å and about 2,000 Å, such as about 200 Å.

Once the first etch stop layer 107 has been formed to cover theconductive elements 105, the second etch stop layer 109 is formed overthe first etch stop layer 107. In an embodiment the second etch stoplayer 109 is formed of a material such as a carbon doped oxide such asSiOC, although any other suitable material may also be used. Thematerial of the second etch stop layer 109 may be formed using adeposition process such as chemical vapor deposition, physical vapordeposition, atomic layer deposition, or the like, and may be depositedto a thickness of between about 10 Å and about 200 Å, such as about 40Å. However, any suitable process of formation and thickness may beutilized.

Once the second etch stop layer 109 has been formed, the third etch stoplayer 110 is formed over the second etch stop layer 109. In anembodiment the third etch stop layer 110 is formed of a material such asaluminum oxide, although any suitable material, such as aluminumnitride, may also be used. The material of the third etch stop layer 110may be formed using a deposition process such as chemical vapordeposition, physical vapor deposition, atomic layer deposition, or thelike, and may be deposited to a thickness of between about 10 Å andabout 200 Å, such as about 40 Å. However, any suitable process offormation and thickness may be utilized.

Once the third etch stop layer 110 has been formed, the first dielectriclayer 111 may be formed in order to help isolate the interconnect 305(not illustrated in FIGS. 1A-1C but illustrated and discussed furtherbelow with respect to FIG. 3) from other adjacent electrical routinglines. In an embodiment the first dielectric layer 111 may be, e.g., alow-k dielectric film intended to help isolate the interconnect 305 fromother structures. By isolating the interconnect 305, theresistance-capacitance (RC) delay of the interconnect 305 may bereduced, thereby improving the overall efficiency and speed ofelectricity through the interconnect 305.

In an embodiment the first dielectric layer 111 may be a porous materialsuch as SiOCN, SiCN or SiOC and may be formed by initially forming aprecursor layer over the third etch stop layer 110. The precursor layermay comprise both a matrix material and a porogen interspersed withinthe matrix material, or may alternatively comprise the matrix materialwithout the porogen. In an embodiment the precursor layer may be formed,e.g., by co-depositing the matrix material and the porogen using aprocess such as plasma enhanced chemical vapor deposition (PECVD) wherethe matrix material is deposited at the same time as the porogen,thereby forming the precursor layer with the matrix material and theporogen mixed together. However, as one of ordinary skill in the artwill recognize, co-deposition using a simultaneous PECVD process is notthe only process that may be used to form the precursor layer. Anysuitable process, such as premixing the matrix material and the porogenmaterial as a liquid and then spin-coating the mixture onto themetallization layers 103, may also be utilized.

The precursor layer may be formed to a thickness sufficient to providethe isolation and routing characteristics that are desired of the firstdielectric layer 111. In an embodiment, the precursor layer may beformed to a first thickness T₁ of between about 10 Å and about 1000 Å,such as about 300 Å. However, these thicknesses are meant to beillustrative only, and are not intended to limit the scope of theembodiments, as the precise thickness of the precursor layer may be anysuitable desired thickness.

The matrix material, or base dielectric material, may be formed using aprocess such as PECVD, although any suitable process, such as a chemicalvapor deposition (CVD), physical vapor deposition (PVD), or even spin-oncoating, may alternatively be utilized. The PECVD process may utilizeprecursors such as methyldiethoxy silane (DEMS), although otherprecursors such as other silanes, alkylsilanes (e.g., trimethylsilaneand tetramethylsilane), alkoxysilanes (e.g., methyltriethoxysilane(MTEOS), methyltrimethoxysilane (MTMOS), methyldimethoxysilane (MDMOS),trimethylmethoxysilane (TMMOS) and dimethyldimethoxysilane (DMDMOS)),linear siloxanes and cyclic siloxanes (e.g.,octamethylcyclotetrasiloxane (OMCTS) and tetramethylcyclotetrasiloxane(TMCTS)), combinations of these, and the like may alternatively beutilized. However, as one of ordinary skill in the art will recognize,the materials and processes listed herein are merely illustrative andare not meant to be limiting to the embodiments, as any other suitablematrix precursors may alternatively be utilized.

After the precursor layer has been formed with the porogen dispersedwithin the matrix material, the porogen is removed from the matrixmaterial to form the pores within the matrix material. In an embodimentthe removal of the porogen is performed by an annealing process whichcan break down and vaporize the porogen material, thereby allowing theporogen material to diffuse and leave the matrix material, therebyleaving behind a structurally intact porous dielectric material as thefirst dielectric layer 111. For example, an anneal of between about 200°C. and about 500° C., such as about 400° C., for between about 10seconds and about 600 seconds, such as about 200 seconds, may beutilized.

However, as one of ordinary skill in the art will recognize, the thermalprocess described above is not the only method that may be utilized toremove the porogen from the matrix material to form the first dielectriclayer 111. Other suitable processes, such as irradiating the porogenwith UV radiation to decompose the porogen or utilizing microwaves todecompose the porogen, may alternatively be utilized. These and anyother suitable process to remove all or a portion of the porogen are allfully intended to be included within the scope of the embodiments.

FIG. 1A additionally illustrates a placement of an anti-reflective layer113. In an embodiment the anti-reflective layer 113 may be anitrogen-free anti-reflective coating and may comprise a polymer resin,a catalyst, and a cross-linking agent, all of which are placed into asolvent for dispersal. The polymer resin comprises a polymer chain withrepeating units, such as a cross-linking monomer and a monomer withchromophore units. In an embodiment the monomer with the chromophoreunit may comprise vinyl compounds containing substituted andunsubstituted phenyl, substituted and unsubstituted anthracyl,substituted and unsubstituted phenanthryl, substituted and unsubstitutednaphthyl, substituted and unsubstituted heterocyclic rings containingheteroatoms such as oxygen, sulfur, or combinations thereof, such aspyranyl or acridinyl. The substituents in these units may be anyhydrocarbyl group and may further contain heteroatoms, such as, oxygen,sulfur or combinations thereof, such as alkylenes, ester, ethers,combinations of these, or the like, with a number of carbon atomsbetween 1 and 12.

The cross-linking monomer may be used to cross-link the monomer withother polymers within the polymer resin to modify the solubility of theanti-reflective layer 113, and may optionally have an acid labile group.In a particular embodiment the cross-linking monomer may comprise ahydrocarbon chain that also comprises, e.g., a hydroxyl group, acarboxyl acid group, a carboxylic ester group, epoxy groups, urethanegroups, amide groups, combinations of the, and the like.

The catalyst may be a compound that is used to generate a chemicallyactive species and initiate a cross-linking reaction between thepolymers within the polymer resin and may be, e.g., a thermal acidgenerator, a photoacid generator, a photobase generator, suitablecombinations of these, or the like. In an embodiment in which thecatalyst is a thermal acid generator, the catalyst will generate an acidwhen sufficient heat is applied to the anti-reflective layer 113.Specific examples of the thermal acid generator include butane sulfonicacid, triflic acid, nanoflurobutane sulfonic acid, nitrobenzyltosylates, such as 2-nitrobenzyl tosylate, 2,4-dinitrobenzyl tosylate,2,6-dinitrobenzyl tosylate, 4-nitrobenzyl tosylate; benzenesulfonatessuch as 2-trifluoromethyl-6-nitrobenzyl 4-chlorobenzenesulfonate,2-trifluoromethyl-6-nitrobenzyl 4-nitro benzenesulfonate; phenolicsulfonate esters such as phenyl, 4-methoxybenzenesulfonate; alkylammonium salts of organic acids, such as triethylammonium salt of10-camphorsulfonic acid, combinations of these, or the like.

The cross-linking agent may also be added to the anti-reflective layer113. The cross-linking agent reacts with the polymers within the polymerresin within the anti-reflective layer 113, assisting in increasing thecross-linking density of the photoresist, which helps to improve theresist pattern and resistance to dry etching. In an embodiment thecross-linking agent may be an melamine based agent, a urea based agent,ethylene urea based agent, propylene urea based agent, glycoluril basedagent, an aliphatic cyclic hydrocarbon having a hydroxyl group, ahydroxyalkyl group, or a combination of these, oxygen containingderivatives of the aliphatic cyclic hydrocarbon, glycoluril compounds,etherified amino resins, a polyether polyol, a polyglycidil ether, avinyl ether, a triazine, combinations of these, or the like.

The materials for the anti-reflective layer 113 may be placed into asolvent for dispersal. In an embodiment the solvent may be an organicsolvent, and may comprise any suitable solvent such as ketones,alcohols, polyalcohols, ethers, glycol ethers, cyclic ethers, aromatichydrocarbons, esters, propionates, lactates, lactic esters, alkyleneglycol monoalkyl ethers, alkyl lactates, alkyl alkoxypropionates, cycliclactones, monoketone compounds that contain a ring, alkylene carbonates,alkyl alkoxyacetate, alkyl pyruvates, lactate esters, ethylene glycolalkyl ether acetates, diethylene glycols, propylene glycol alkyl etheracetates, alkylene glycol alkyl ether esters, alkylene glycol monoalkylesters, or the like.

Once the material for the anti-reflective layer 113 has been prepared,the material for the anti-reflective layer 113 may be utilized byinitially applying the material for the anti-reflective layer 113 ontothe first dielectric layer 111. The material for the anti-reflectivelayer 113 may be applied to the first dielectric layer 111 so that thematerial for the anti-reflective layer 113 coats an upper exposedsurface of the first dielectric layer 111, and may be applied using aprocess such as a spin-on coating process, a dip coating method, anair-knife coating method, a curtain coating method, a wire-bar coatingmethod, a gravure coating method, a lamination method, an extrusioncoating method, combinations of these, or the like. In an embodiment thematerial for the anti-reflective layer 113 may be applied such that ithas a thickness of between about 50 nm and about 500 nm, such as about300 nm.

Once the anti-reflective layer 113 has been formed, a first hardmask 115may be formed over the anti-reflective layer 113. In an embodiment thefirst hardmask 115 may be a masking material with a different etchingselectivity from the material of the second etch stop layer 109, such astitanium nitride (TiN), although any other suitable material, such astitanium oxide may be used. The first hardmask 115 may be formed using adeposition process such as chemical vapor deposition, physical vapordeposition, atomic layer deposition, combinations of these, or the like,and may be formed to an initial second thickness T₂ of between about 50Å and about 800 Å, such as about 300 Å. However, any suitable thicknessmay be utilized.

Once formed, the first hardmask 115 may be patterned in order to providea masking layer for a subsequent etching process (e.g. a first etchingprocess 121 described below) to form a via opening 119. In an embodimentthe first hardmask 115 may be patterned by placing a first photoresist118 over the first hardmask 115 and then exposing and developing thefirst photoresist 118 to form a patterned photoresist. In an embodimentthe first photoresist 118 is a tri-layer photoresist, with a bottomanti-reflective coating (BARC) layer, an intermediate mask layer, and atop photoresist layer (not separately illustrated within FIG. 1A).However, any suitable type of photosensitive material or combination ofmaterials may be utilized. Once the first photoresist 118 has beenpatterned, the pattern of the first photoresist 118 is then transferredto the first hardmask 115 using, e.g., an anisotropic etching processsuch as a reactive ion etching process. However, any suitable processmay be utilized.

In an embodiment the first hardmask 115 may be patterned to form a maskfor the via opening 119. As such, the first hardmask 115 may bepatterned such that the via opening 119 has a first width W₁ of betweenabout 10 nm and about 40 nm, such as about 25 nm. However, any suitabledimensions may be utilized.

Once the first hardmask 115 has been patterned, the pattern of the firsthardmask 115 may be transferred to the first dielectric layer 111 usinga first etching process (represented in FIG. 1A by the wavy lineslabeled 121). In an embodiment the first etching process 121 may be,e.g., an anisotropic etching process such as a reactive ion etch withetchants suitable to etch the first dielectric layer 111. However, anysuitable etching method or combination of etching methods may beutilized.

By using the first etch process 121 and the first hardmask 115, thepattern of the first hardmask 115 is transferred to the anti-reflectivelayer 113 and then to the first dielectric layer 111 and the via opening119 is formed. In an embodiment the transfer of the pattern from thefirst hardmask 115 into the first dielectric layer 111 helps to form thevia portion 307 of the interconnect 305 into the first dielectric layer111. In a particular embodiment, the via portion 307 of the interconnect305 may be formed by the first etch process 121 to extend into the firstdielectric layer 111 a first depth D₁ of between about 200 Å and about2000 Å, such as about 800 Å. However, any suitable depth may beutilized.

FIG. 1B illustrates that, once the via opening 119 has been formed, thefirst photoresist 118 is removed. In an embodiment the first photoresist118 is removed using a process such as ashing, whereby the temperatureof the first photoresist 118 is increased until the first photoresist118 experiences a thermal decomposition, at which point the firstphotoresist 118 may be easily removed. However, any other suitableprocess, such as a wet or dry etch, or even removing the firstphotoresist 118 using the same etching process that forms the viaopening 119, may be used.

Once the first photoresist 118 has been removed, a second photoresist125 may be deposited and patterned to form openings to assist in thepatterning of trench openings 129. In an embodiment the secondphotoresist 125 is a tri-layer photoresist, with a bottomanti-reflective coating (BARC) layer, an intermediate mask layer, and atop photoresist layer (not separately illustrated within FIG. 1B).However, any suitable type of photosensitive material or combination ofmaterials may be utilized.

Once the second photoresist 125 has been placed over the first hardmask115 and the via opening 119, the second photoresist 125 is patterned. Inan embodiment the second photoresist 125 may be patterned by exposing aphotosensitive material within the second photoresist 125 (e.g., the topphotoresist layer in the tri-layer photoresist) to a patterned energysource (e.g., light) through, e.g., a reticle. The impact of the energywill cause a chemical reaction in those parts of the photosensitivematerial that were impacted by the patterned energy source, therebymodifying the physical properties of the exposed portions of thephotoresist such that the physical properties of the exposed portions ofthe second photoresist 125 are different from the physical properties ofthe unexposed portions of the second photoresist 125. The secondphotoresist 125 may then be developed with, e.g., a developer (notseparately illustrated), in order to separate the exposed portion of thesecond photoresist 125 from the unexposed portion of the secondphotoresist 125, and the pattern of the top photoresist layer may beextended through the intermediate mask layer and the bottomanti-reflective coating layer.

In an embodiment the second photoresist 125 may be patterned such thatthe second photoresist 125 can be used to form the trench openings 129through the first dielectric layer 111. As such, the second photoresist125 may be formed to have openings with a second width W₂ of betweenabout 40 nm and about 150 nm, such as about 50 nm. However, any suitabledimensions may be utilized.

Once the second photoresist 125 has been placed and patterned, a secondetching process (represented in FIG. 1B by the wavy lines labeled 127)may be used to form trench openings 129 which will be filled to form viaportions 303 of the interconnect 305. In an embodiment the secondetching process 127 may be similar to the first etching process 121. Forexample, the second etching process 127 may be an anisotropic etchingprocess such as a reactive ion etching process that utilizes etchantsthat are selective to the first dielectric layer 111.

The second etching process 127 will work to form the trench openings 129and also extend the via opening 119 all of the way through the firstdielectric layer 111 and will expose the underlying third etch stoplayer 110, which material is chosen to stop or at least slow down thesecond etching process 127 and prevent the second etching process 127from etching past the third etch stop layer 110. As such, the viaopenings 119 may extend into, but not through, the third etch stop layer110.

FIG. 1C additionally illustrates that the via openings 119 may beextended through the third etch stop layer 110 and the second etch stoplayer 109. In an embodiment the breakthrough of the via openings 119through the third etch stop layer 110 and the second etch stop layer 109is performed with one or more wet etching processes in which liquidetchants are brought into contact with the third etch stop layer 110 andthen the second etch stop layer 109.

After the third etch stop layer 110 and the second etch stop layer 109have been patterned to extend the via openings 119, the via openings 119may be extended through the first etch stop layer 107. In an embodimentthe extension of the via openings 119 through the first etch stop layer107 exposes the underlying conductive elements 105, and may be performedusing, e.g., a wet or dry etching process, although any suitable methodmay be utilized.

Once the conductive elements 105 have been exposed, a liner removal maybe performed in order to remove any material from the first dielectriclayer 111 that may have entered the trench openings 129 and via openings119. In an embodiment the liner removal may be performed using anetching process such as a dry etch. For example, in an embodiment theliner removal dry etch may clean the openings as well as at leastpartially round the corners of the via openings 119 and the trenchopenings 129. However, any suitable dimensions may be used.

FIGS. 1C and 2A-2C illustrate that, once the conductive elements 105have been exposed and the liner removal has been performed, the secondphotoresist 125 is removed using a cleaning/stripping process that bothremoves the second photoresist 125 as well as remove any remainingresidue 131 left over from the previous processes (e.g., the etchingresidue), clean and pre-clean the surfaces of the trench openings 129and the via openings 119 prior to placement of a first barrier layer 301(not illustrated in FIGS. 2A-2C but described below with respect to FIG.3), and, optionally, release charges that may have accumulated on theexposed surfaces. In an embodiment the cleaning process may comprise awet cleaning process 250 (also called a wet etch cleaning process)followed by a plasma treatment, both of which are performed in a single,all-in-one, combined process machine 200 without breaking to an exterioratmosphere. For example, as illustrated in FIG. 2A, the combined processmachine 200 comprises both a wet etching section 202 and a plasmatreatment section 204, along with a transfer station 206 between the wetetching section 202 and the plasma treatment section 204, all of whichare encased within an exterior housing 281 that separates the wetetching section 202, the plasma treatment section 204, and the transferstation 206 from an exterior environment.

In an embodiment the wet etching section 202 comprises a feed tank 210in order to provide a suitable supply of a first etchant to each of aplurality of wet etching stations 208. The first etchant is utilized inorder to remove the residues 131 from within the via opening 119 and thetrench opening 129 and, as such, is at least partially dependent uponthe materials and products utilized during the previous processes.However, in an embodiment in which the first etch stop layer 107 isaluminum oxynitride, the conductive elements 105 are copper, and theresidues are a fluorinated polymer, the first etchant may be a solutioncomprising an oxidizer and a solvent.

For example, in an embodiment the oxidizer may be hydrogen peroxide,although any other suitable oxidizer, such as ozone water or phosphatesalts, may also be used. In an embodiment the oxidizer may be placedwithin the solution at a concentration of less than about 25%, such asabout 15%. However, any suitable concentration may be utilized.

The organic solvent is utilized to dilute and deliver the oxidizer. Inan embodiment the organic solvent may be an organic liquid such asethylene glycol, propylene glycol monomethyl ether, diethylene glycolmonoethyl ether, diethylene glycol monobutyl ether,tetrahydrothiophene-1,1-dioxide, dimethylsulfoxide,N—N-dimethylacetamide, 4-methylmorpholine, 4-methylmorpholine N-oxide,4-methoxypyridine-N-oxide hydrate, ammonium hydroxide, tetramethylammonium hydroxide, tetraethylammonium hydroxide, mixtures of these, orthe like. The organic solvent may be within the solution at aconcentration of between about 5% and about 50%, such as about 30%.However, any suitable material and concentration may be utilized.

Optionally, other additives may be placed into the solution for thefirst etchant. For example, etching inhibitors such as benzotriazole orimidazole may be placed into the solution in order to better control theetching characteristics of the first etchant. Any suitable additives maybe added to the solution for the first etchant.

The first etchant may be placed into the feed tank 210 (otherwise knownas a day tank) through a first input 212 connected to a suitablefacility. Optionally, if the components of the first etchant (e.g., theoxidizer, the organic solvent, and any other additives) are received asseparate components, an optional mixing unit (not separatelyillustrated) may be placed upstream from the feed tank 210. In thisembodiment the individual components are placed within the mixing unitand mixed prior to being placed into the feed tank 210.

The feed tank 210 additionally has a second input 214 to recycle firstetchant which has been used by the wet etching stations 208. Forexample, the second input 214 to the feed tank 210 is connected torespective outputs from each of the wet etching stations 208 so that,once the first etchant has been used within the wet etching stations 208during, e.g., the wet cleaning process 250, the used first etchant canbe recycled back to the feed tank 210 for recycling.

In order to help recover the used first etchant so that the firstetchant can be recycled for another use, the feed tank 210 alsocomprises a third input 216 (and an associated flow meter 217) toreceive additional components for the first etchant in order to recoverthe effectiveness of the first etchant. For example, additional amountsof the oxidizer (an oxidizer spike) may be entered through the thirdinput 216 in order to raise the concentration of the oxidizer within thefeed tank 210 and help reclaim any of the oxidizer that was used orotherwise lost during the wet cleaning process 250 within the wetetching stations 208.

Similarly, additional amounts of the solvent or any other additives mayalso be spiked in order to reclaim or otherwise retain the ability ofthe first etchant to perform as desired. In some embodiments, samples ofthe first etchant (from either the day tank or from the wet etchingstations 208) may be taken and analyzed, and a makeup amount, if needed,for each component may be determined. Such a makeup amount of eachcomponent may then be added through the third input 216.

A first output 218 from the feed tank 210 is routed to a respectiveinput of each of the wet etching stations 208 (described further belowwith respect to FIG. 2B) in order to supply each of the wet etchingstations 208 with fresh first etchant for the wet cleaning process 250performed within the wet etching stations 208. Optionally, the firstoutput 218 also comprises additional units which help to control thephysical characteristics of the first etchant after it leaves the feedtank 210 and prior to the first etchant being used in the wet cleaningprocess 250. For example, the first output 218 may comprise a first pump262 to control the flow rate of the first etchant, a first heater 264 inorder to control the temperature of the first etchant, and a firstfilter 266 in order to help purify the first etchant. However, anysuitable control systems may be utilized.

The first output 218 supplies the first etchant to a number of wetetching stations 208. In the embodiment illustrated in FIG. 2A, thefirst output 218 supplies the first etchant to four wet etching stations208. However, this number of wet etching stations 208 is intended to beillustrative only. Any suitable number of wet etching stations 208 maybe utilized within the wet etching section 202 of the combined processmachine 200.

FIG. 2B illustrates a top-down view of one embodiment of a single wetetching station 208. In this embodiment the wet etching station 208 is aspin-on station and comprises a rotating chuck 224, a dispensing arm226, and a track 232. The rotating chuck 224 receives the substrate 101and holds the substrate 101 during processing.

The dispensing arm 226 has a nozzle 228 in order to dispense the firstetchant onto the substrate 101 such that the first etchant comes intophysical contact with the residue 131. In an embodiment the dispensingarm 226 may be moveable relative to the rotating chuck 224 so that thedispensing arm 226 can move over the substrate 101 (illustrated in FIG.2B by the arrow and dispensing arm illustrated in dashed lines) in orderto evenly dispense the first etchant. The dispensing arm 226 may moveback and forth with the help of the track 232, which provides a fixedreference to assist the dispensing arm 226 in its movement.

During the wet cleaning process 250, the substrate 101 is placed ontothe rotating chuck 224 and the rotating chuck 224, holding the substrate101, rotates at a speed of between about 100 rpms and about 1000 rpms,such as about 500 rpms, although any suitable speed may be utilized.While the rotating chuck 224 is rotating, the dispensing arm 226 maymove over the substrate 101 and begin dispensing the first etchant ontothe substrate 101 through the nozzle 228. The rotation of the substrate101 helps the first etchant to spread evenly across the substrate 101and reduce cleaning variations from uneven dispersal of the firstetchant.

In an embodiment the first etchant may be dispersed at a temperature ofbetween about 25° C. and about 60° C., such as about 50° C.Additionally, the first etchant may be dispensed at a flow rate ofbetween about 500 mL/min and about 2500 mL/min, such as about 1500mL/min. To help ensure removal of the residues 131, the wet cleaningprocess 250 may continue for a time of between about 30 s and about 240s, such as about 120 s. However, any suitable process conditions andtime periods may also be utilized.

Additionally, as one of ordinary skill in the art will recognize, thespin-on configuration illustrated in FIG. 2B and described above isintended to be illustrative only and is not intended to limit theembodiments. Rather, any suitable configuration for the wet etchingstation 208 that may be used to apply the first etchant, such as a dipcoating configuration, an air-knife coating configuration, a curtaincoating configuration, a wire-bar coating configuration, a gravurecoating configuration, a lamination configuration, an extrusion coatingconfiguration, combinations of these, or the like, may alternatively beutilized. All such suitable configuration for the wet etching station208 are fully intended to be included within the scope of theembodiments.

Once the wet cleaning process 250 has been completed, the first etchantmay be removed and the substrate 101 may be dried prior to removal fromthe wet etching station 208. In an embodiment the substrate 101 may bedried by stopping the flow of the first etchant through the nozzle 228while maintaining at least a partial rotation to spin-off the remainingfirst etchant. Additionally, if desired, a rinsing material, such asdeionized water, may also be dispensed onto the substrate 101 to aid inthe removal of the first etchant. Finally, a drying process such asdispensing a drying material such as IPA along with an application ofnitrogen (N2), may be utilized to dry the substrate 101. However, anysuitable method of removing the first etchant and drying the substrate101 may be utilized.

Returning to FIG. 2A, once the wet cleaning process 250 has beencompleted within the wet etching station 208, the substrate 101 may beremoved from the wet etching station 208 by the transfer station 206. Inan embodiment the transfer station 206 may be one or more robotic arms(not individually illustrated in FIG. 2A) that can grip, move, andtransfer the substrate 101 from the wet etching station 208 to, e.g.,the plasma treatment section 204. In an embodiment the robotic arms mayextend into the wet etching station 208, grip the substrate 101, andtransfer the substrate 101 into the transfer station 206. Once inside,the transfer station 206 may have doors that close to isolate thetransfer station 206 from the wet etching station 208 so that the wetetching station 208 may again be opened for further processing. Onceisolated from the wet etching station 208, the transfer station 206 mayopen to the next station, e.g., the plasma treatment system 201, and therobotic arms, still holding the substrate 101, may extend into the nextstation and deposit the substrate 101 for further processing.

FIG. 2C illustrates an embodiment of one of the plurality of plasmatreatment systems 201 (along with the inputs and exhausts) that may beused in order to treat the exposed surfaces. In an embodiment the plasmatreatment system 201 may comprise a treatment gas delivery system 203that may deliver one or more treatment gases to a plasma treatmentchamber 254. The treatment gas delivery system 203 supplies the variousdesired treatment gases to the plasma treatment chamber 254 through atreatment gas controller 213 and a manifold 205. The treatment gasdelivery system 203 may also help to control the flow rate of thetreatment gases into the plasma treatment chamber 254 by controlling theflow and pressure of a carrier gas through the treatment gas deliverysystem 203.

In an embodiment the treatment gas delivery system 203 may include aplurality of treatment gas suppliers 211 along with an optional carriergas supply 207. Additionally, while only two treatment gas suppliers 211are illustrated in FIG. 2C, this is done merely for clarity, as anysuitable number of treatment gas suppliers 211, such as one treatmentgas supplier 211 for each treatment gas desired to be used within theplasma treatment system 201, may be used. For example, in an embodimentin which five separate treatment gases will be utilized, there may befive separate treatment gas suppliers 211.

Each of the individual treatment gas suppliers 211 may be a vessel, suchas a gas storage tank, that is located either locally to the plasmatreatment chamber 254 or remotely from the plasma treatment chamber 254.Alternatively, the treatment gas supplier 211 may be a facility thatindependently prepares and delivers the desired treatment gases. Anysuitable source for the desired treatment gases may be utilized as thetreatment gas supplier 211, and all such sources are fully intended tobe included within the scope of the embodiments.

In an embodiment the individual treatment gas suppliers 211 supply atreatment gas to the treatment gas controller 213 through first lines252 with first valves 258. The first valves 258 are controlled by acontroller 227 that controls and regulates the introduction of thevarious treatment and carrier gases to the plasma treatment chamber 254.

Optionally, in embodiments in which the treatment gas within thetreatment gas suppliers 211 are not inert gases themselves, a carriergas supply 207 may supply a desired carrier gas, or diluent gas, thatmay be used to help push or “carry” the various desired treatment gasesto the plasma treatment chamber 254. The carrier gas may be an inert gasor other gas that does not react with the treatment gases or withby-products from the reactions of the treatment gases. For example, thecarrier gas may be nitrogen (N₂), helium (He), argon (Ar), combinationsof these, or the like, although other suitable carrier gases may beutilized.

The carrier gas supply 207, or diluent supply, may be a vessel, such asa gas storage tank, that is located either locally to the plasmatreatment chamber 254 or remotely from the plasma treatment chamber 254.Alternatively, the carrier gas supply 207 may be a facility thatindependently prepares and delivers the carrier gas to the treatment gascontroller 213. Any suitable source for the carrier gas may be utilizedas the carrier gas supply 207, and all such sources are fully intendedto be included within the scope of the embodiments. The carrier gassupply 207 may supply the desired carrier gas to the treatment gascontroller 213 through a second line 260 with a second valve 256 thatconnects the carrier gas supply 207 to the first lines 252. The secondvalve 256 is also controlled by the controller 227 that controls andregulates the introduction of the various etchants and carrier gases tothe plasma treatment chamber 254. Once combined, the lines may bedirected towards the treatment gas controller 213 for a controlled entryinto the plasma treatment chamber 254.

The plasma treatment chamber 254 may be any desired shape that may besuitable for dispersing the treatment gases and contacting the treatmentgases with the substrate 101. In the embodiment illustrated in FIG. 2C,the plasma treatment chamber 254 has a cylindrical sidewall and abottom. However, the plasma treatment chamber 254 is not limited to acylindrical shape, and any other suitable shape, such as a hollow squaretube, an octagonal shape, or the like, may alternatively be utilized.Furthermore, the plasma treatment chamber 254 may be surrounded by achamber housing 215 made of material that is inert to the variousprocess materials. As such, while the chamber housing 215 may be anysuitable material that can withstand the chemistries and pressuresinvolved in the treatment process, in an embodiment the chamber housing215 may be steel, stainless steel, nickel, aluminum, alloys of these,combinations of these, and the like.

Within the plasma treatment chamber 254 is located a mounting platform245 in order to position and control the substrate 101 during thenon-liquid, plasma treatment process 270. The mounting platform 245 mayhold the substrate 101 using a combination of clamps, vacuum pressure,and/or electrostatic forces, and may also include heating and coolingmechanisms in order to control the temperature of the substrate 101during the processes. In a particular embodiment the mounting platform245 may comprise four cooling zones, such as an inner temperature zone,a middle inner temperature zone, a middle outer temperature zone, and anouter temperature zone (not individually illustrated) in order to heatand cool the substrate 101 during the treatment process. The varioustemperature zones may use gaseous or liquid heat transfer materials toprecisely control the temperature of the substrate 101 during thetreatment process, although any suitable number of heating or coolingzones may alternatively be utilized.

The mounting platform 245 may additionally comprise a first electrode220 coupled to a first RF generator 222. The first electrode 220 may beelectrically biased by the first RF generator 222 (under control of thecontroller 227) at a RF voltage during the plasma treatment process 270.By being electrically biased, the first electrode 220 is used to providea bias to the incoming treatment gases and assist to ignite them into aplasma. Additionally, the first electrode 220 is also utilized tomaintain the plasma during the plasma treatment process 270 bymaintaining the bias.

Furthermore, while a single mounting platform 245 is illustrated in FIG.2C, this is merely intended for clarity and is not intended to belimiting. Rather, any number of mounting platforms 245 may additionallybe included within the plasma treatment chamber 254. As such, multiplesemiconductor substrates may be etched during a single plasma treatmentprocess.

Additionally, the plasma treatment chamber 254 comprises a showerhead229. In an embodiment the showerhead 229 receives the various treatmentgases from the manifold 205 (through, e.g., treatment heater 272) andhelps to disperse the various treatment gases into the plasma treatmentchamber 254. The showerhead 229 may be designed to evenly disperse thetreatment gases in order to minimize undesired process conditions thatmay arise from uneven dispersal. In an embodiment the showerhead 229 mayhave a circular design with openings dispersed evenly around theshowerhead 229 to allow for the dispersal of the desired treatment gasesinto the plasma treatment chamber 254.

The plasma treatment chamber 254 also comprises an upper electrode 221,for use as a plasma generator. In an embodiment the plasma generator maybe a transformer coupled plasma generator and may be, e.g., a coil. Thecoil may be attached to a second RF generator 223 that is utilized toprovide power to the upper electrode 221 (under control of thecontroller 227) in order to ignite the plasma during introduction of thetreatment gases.

However, while the upper electrode 221 is described above as atransformer coupled plasma generator, embodiments are not intended to belimited to a transformer coupled plasma generator. Rather, any suitablemethod of generating the plasma, such as inductively coupled plasmasystems, magnetically enhanced reactive ion etching, electron cyclotronresonance, a remote plasma generator, or the like, may alternatively beutilized. All such methods are fully intended to be included within thescope of the embodiments.

The plasma treatment chamber 254 may also be connected to one or morevacuum pumps 225 for exhaust from the plasma treatment chamber 254. Inan embodiment the vacuum pump 225 is under the control of the controller227, and may be utilized to control the pressure within the plasmatreatment chamber 254 to a desired pressure. Additionally, once thetreatment process is completed, the vacuum pump 225 may be utilized toevacuate the plasma treatment chamber 254 in preparation for removal ofthe substrate 101.

The plasma treatment process (represented in FIG. 2C by the wavy lineslabeled 270 may be initiated by placing the desired treatment gases intothe treatment gas suppliers 211 while placing the desired diluent intothe carrier gas supply 207. As such, while the precise treatment gasesand carrier gases are dependent at least in part upon the materials ofthe overlying structure (e.g., the first etch stop layer 107, theconductive elements 105, the second etch stop layer 109, etc.) and theresidue 131, in a particular embodiment in which the first etch stoplayer 107 is aluminum oxynitride and the conductive elements 105 arecopper, treatment gases such as N₂, H₂, CH₄, O₂, ozone, Ar, Air, N₂H₂,N₂H₄, C_(x)F_(y), combinations of these, or the like, may be placedwithin the treatment gas suppliers 211. Additionally, in embodiments inwhich the treatment gases are non-reactive, the carrier gas may be anon-reactive gas such as argon, helium, combinations of these, or thelike, and may be placed into the carrier gas supply 207. However, anysuitable treatment gases and diluents may be utilized.

Optionally, or sequentially if desired, the treatment gases may bechosen so as to releases charges that might have built up duringprevious processes and may cause defects. In one embodiment thetreatment gases are chosen based on the treatment gases ability toeither neutralize the charges that are already present or else at leastdo not generate additional charges during the plasma treatment process270. In particular embodiments the treatment gases may be chosen to becations or anions such as nitrogen (N₂) or hydrogen (H₂), which releaseany charges that are already present.

Once the treatment gas or gases have been placed within the treatmentgas suppliers 211, the plasma treatment process 270 may be initiated bythe controller 227 connecting the desired treatment gas suppliers 211and, optionally, the carrier gas supply 207 to the plasma treatmentchamber 254. In a particular embodiment the treatment gas may beintroduced to the plasma treatment chamber 254 at a flow rate of betweenabout 100 mL/h and about 300 mL/h, such as about 250 mL/h. Additionally,the plasma treatment chamber 254 may be kept at a process temperature ofbetween about 25° C. and about 80° C., such as about 30° C., and aprocess pressure of between about 0.1 Torr and about 100 Torr, such asabout 50 Torr. However, any suitable flow rates, temperatures, andpressures may be utilized.

Once the treatment gases have been introduced into the plasma treatmentchamber 254, the treatment gases may be ignited into the plasma. In anembodiment the controller 227 may begin by first applying an RF power at60 MHz (the source power at the upper electrode 221) of between about100 W and about 1000 W, such as about 200 W and applying an RF power at2 MHz (the bias power at the first electrode 220) of between about 100 Wand about 1000 W, such as about 200 W. The ignition step may bemaintained for a time of between about 1 s and about 100 s, such asabout 2 seconds in order to ensure ignition of the plasma.

Once ignition has occurred, the plasma treatment process 270 may beutilized to treat the exposed surfaces and ensure that any remainingresidues 131 are removed from the via openings 119 and the trenchopenings 129. In an embodiment the plasma treatment process 270,controlled by the controller 227, sets the RF power at 60 MHz to betweenabout 200 W and about 2000 W, such as about 1500 W and also setting theRF power at 2 MHz to between about 200 W and about 2000 W, such as about1500 W. The plasma treatment process 270 will proceed with treating theexposed surfaces for a time of between about 5 s and about 100 s, suchas about 45 seconds. However, any suitable process parameters and timeperiods may be utilized.

Additionally, while a specific embodiment of the etching process hasbeen described above with respect to FIG. 2C, these discussions areintended to be illustrative only and are not intended to be limitingupon the embodiments. Rather, any suitable combination of etchants,carrier gases, and process conditions may be utilized. All suchcombinations are fully intended to be included within the scope of theembodiments.

By utilizing the wet stripping process along with the plasma treatment,defects from the presence of the polymeric residues may be reduced oreven completed eliminated. Further, metal corrosion (e.g., oxidation) orgalvanic effects that occur due to the presence of a wet strip anddeionized water rinse may also be avoided. Finally, abnormal film lossbecause of incoming charging from dry etching can be avoided through thecharge release. All of this helps achieve a better adhesion and coverageof later deposited materials (e.g., the first barrier layer 301 andconductive material, described further below with respect to FIG. 3).

Additionally, while the above described cleaning process is described ascomprising the wet cleaning process 250 occurring prior to the plasmatreatment process 270, this is intended to be illustrative and is notintended to be limiting. Rather, any suitable order of process steps,such as performing the plasma treatment process 270 before the wetcleaning process 250, may also be utilized. Any suitable order ofprocess steps is fully intended to be included within the scope of theembodiments.

After the cleaning process has been completed, the first barrier layer301 may be deposited in order to help isolate and protect a subsequentlyformed conductive material (discussed further below). In an embodimentthe first barrier layer 301 may comprise a barrier material such astitanium, titanium nitride, combinations of these, or the like, and maybe formed using a process such as chemical vapor deposition (CVD),physical vapor deposition (PVD), atomic layer deposition (ALD), or thelike. The first barrier layer 301 may be formed to have a thickness ofbetween about 0.1 μm and about 20 μm, such as about 0.5 μm.

Once the first barrier layer 301 has been formed to line the trenchopenings 129 and the via openings 119, the trench openings 129 and thevia openings 119 are filled with a conductive material to form theinterconnect 305 with a via portion 307 (within the via openings 119)and the trench portion 303 (within the trench opening 129, andillustrated as being separated from the via portion 307 using a dashedline, although there may or may not be a physical indication of theseparation). The conductive material may comprise copper, although othersuitable materials such as aluminum, alloys, doped polysilicon,combinations thereof, and the like, may alternatively be utilized. Theconductive material may be formed by depositing a seed layer (notseparately illustrated), electroplating copper onto the seed layer, andfilling and overfilling the trench openings 129 and the via opening 119.Once the trench openings 129 and the via opening 119 have been filled,excess portions of the first barrier layer 301, the seed layer, andconductive material outside of the trench openings 129 and the viaopening 119 may be removed through a planarization process such aschemical mechanical polishing (CMP), although any suitable removalprocess may be used.

In an embodiment, a semiconductor device manufacturing tool includes afirst wet etch cleaning station; a first plasma treatment station; and atransfer station operationally located between the first wet etchcleaning station and the first plasma treatment station; and an exteriorhousing surrounding all of the first wet etch cleaning station, thefirst plasma treatment station, and the transfer station. In anembodiment, the semiconductor device manufacturing tool further includesa second wet etch cleaning station. In an embodiment, the semiconductordevice manufacturing tool further includes a feed tank operationallyconnected to both the first wet etch cleaning station and the second wetetch cleaning station. In an embodiment, the semiconductor devicemanufacturing tool further includes a second plasma treatment station.In an embodiment, the semiconductor device manufacturing tool furtherincludes a first treatment gas supplier operationally connected to boththe first plasma treatment station and the second plasma treatmentstation. In another embodiment, the first treatment gas suppliercontains a charge release treatment gas. In another embodiment the firstwet etch cleaning station is a spin-on station.

In an embodiment, a semiconductor device manufacturing tool includes awet etch section comprising a plurality of wet etching chambers; a firsttransfer station located to operate cooperatively with at least one ofthe wet etching chambers; and a plasma treatment section comprising aplurality of plasma treatment chambers, wherein at least one of theplurality of plasma treatment chambers is located to operatecooperatively with the first transfer station, wherein the wet etchsection, the first transfer station, and the plasma treatment sectionare part of a single machine. In an embodiment, the semiconductor devicemanufacturing tool further includes a feed tank connected to each of thewet etching chambers. In an embodiment, the semiconductor devicemanufacturing tool further includes a first input to the feed tank; asecond input to the feed tank; and a third input to the feed tank. Inanother embodiment, the first input is connected to a mixing unit. Inanother embodiment, the second input is a spike input. In anotherembodiment, the third input is a recycle input from the wet etchingchambers. In another embodiment, at least one of the wet etchingchambers comprises a rotatable chuck.

In another embodiment a method of manufacturing a semiconductor device,the method includes forming an opening through a dielectric layer toexpose a conductive element of a semiconductor wafer; placing thesemiconductor wafer into a first processing tool; wet cleaning thesemiconductor wafer within the first processing tool; plasma cleaningthe semiconductor wafer within the first processing tool; and removingthe semiconductor wafer from the first processing tool after the plasmacleaning the semiconductor wafer. In another embodiment, the wetcleaning is performed at least in part using a spin on process. Inanother embodiment, the spin on process comprises contacting a wetetchant onto the semiconductor wafer. In another embodiment, thecontacting the wet etchant comprises removing the wet etchant from afeed tank. In another embodiment, the plasma cleaning releases chargeson the semiconductor wafer. In another embodiment, the plasma cleaninggenerates a plasma from nitrogen or hydrogen.

In another embodiment a method of manufacturing a semiconductor device,the method includes exposing a conductive layer through a dielectriclayer over a semiconductor wafer; removing residue by contacting aliquid etchant to the dielectric layer and the conductive layer, whereinthe contacting the liquid etchant is performed in a first wet etchingchamber of a first processing tool; and performing a plasma cleaningafter the removing the residue, wherein the performing the plasmacleaning is performed within a plasma treatment chamber of the firstprocessing tool. In another embodiment, the plasma cleaning is performedusing oxygen. In another embodiment, the plasma cleaning releasescharges from dielectric layer. In another embodiment, the plasmacleaning is performed at least in part using the plasma of nitrogen orhydrogen. In another embodiment, the liquid etchant comprises an oxidantwithin a solvent. In another embodiment, the liquid etchant furthercomprises an inhibitor. In another embodiment, the residue is afluorinated polymer.

In another embodiment a method of cleaning a semiconductor waferincludes placing a semiconductor wafer onto a spin chuck; dispensing awet etchant onto the semiconductor wafer while the semiconductor waferis spinning; removing the semiconductor wafer from the spin chuck andplacing the semiconductor wafer onto a mounting platform within a plasmatreatment chamber without breaking to an external atmosphere; and plasmatreating the semiconductor wafer. In another embodiment, the plasmatreating the semiconductor wafer further comprises releasing chargesfrom the semiconductor wafer. In another embodiment, the plasma treatingcomprises generating a plasma from nitrogen. In another embodiment, theplasma treating comprises generating a plasma from hydrogen. In anotherembodiment, the dispensing the wet etchant comprises dispensing anoxidant. In an embodiment, the method further includes depositing afirst barrier layer after the plasma treating the semiconductor wafer.In an embodiment, the method further includes plating a conductivematerial onto the first barrier layer.

In another embodiment a method of cleaning a semiconductor deviceincludes placing a semiconductor device into a first processing tool;moving the semiconductor device to a wet etching section of the firstprocessing tool; moving the semiconductor device to a plasma treatmentsection of the first processing tool; and removing the semiconductordevice from the first processing tool. In an embodiment, the methodfurther includes removing residue from the semiconductor device whilethe semiconductor device is located within the wet etching section. Inan embodiment, the method further includes releasing charges from thesemiconductor device while the semiconductor device is located withinthe plasma treatment section of the first processing tool. In anotherembodiment, the releasing charges from the semiconductor device furthercomprises generating a plasma from nitrogen or hydrogen. In anotherembodiment, the moving the semiconductor device to the wet etchingsection is performed prior to the moving the semiconductor device to theplasma treatment section of the first processing tool. In anotherembodiment, the moving the semiconductor device to the wet etchingsection is performed after the moving the semiconductor device to theplasma treatment section of the first processing tool.

The foregoing outlines features of several embodiments so that thoseskilled in the art may better understand the aspects of the presentdisclosure. Those skilled in the art should appreciate that they mayreadily use the present disclosure as a basis for designing or modifyingother processes and structures for carrying out the same purposes and/orachieving the same advantages of the embodiments introduced herein.Those skilled in the art should also realize that such equivalentconstructions do not depart from the spirit and scope of the presentdisclosure, and that they may make various changes, substitutions, andalterations herein without departing from the spirit and scope of thepresent disclosure.

What is claimed is:
 1. A semiconductor device manufacturing toolcomprising: a first wet etch cleaning station; a first plasma treatmentstation; a transfer station operationally located between the first wetetch cleaning station and the first plasma treatment station; and anexterior housing surrounding all of the first wet etch cleaning station,the first plasma treatment station, and the transfer station.
 2. Thesemiconductor device manufacturing tool of claim 1, further comprising asecond wet etch cleaning station.
 3. The semiconductor devicemanufacturing tool of claim 2, further comprising a feed tankoperationally connected to both the first wet etch cleaning station andthe second wet etch cleaning station.
 4. The semiconductor devicemanufacturing tool of claim 1, further comprising a second plasmatreatment station.
 5. The semiconductor device manufacturing tool ofclaim 4, further comprising a first treatment gas supplier operationallyconnected to both the first plasma treatment station and the secondplasma treatment station.
 6. The semiconductor device manufacturing toolof claim 5, wherein the first treatment gas supplier contains a chargerelease treatment gas.
 7. The semiconductor device manufacturing tool ofclaim 1, wherein the first wet etch cleaning station is a spin-onstation.
 8. A semiconductor device manufacturing tool comprising: a wetetch section comprising a plurality of wet etching chambers; a firsttransfer station located to operate cooperatively with at least one ofthe wet etching chambers; and a plasma treatment section comprising aplurality of plasma treatment chambers, wherein at least one of theplurality of plasma treatment chambers is located to operatecooperatively with the first transfer station, wherein the wet etchsection, the first transfer station, and the plasma treatment sectionare part of a single machine.
 9. The semiconductor device manufacturingtool of claim 8, further comprising a feed tank connected to each of thewet etching chambers.
 10. The semiconductor device manufacturing tool ofclaim 9, further comprising: a first input to the feed tank; a secondinput to the feed tank; and a third input to the feed tank.
 11. Thesemiconductor device manufacturing tool of claim 10, wherein the firstinput is connected to a mixing unit.
 12. The semiconductor devicemanufacturing tool of claim 11, wherein the second input is a spikeinput.
 13. The semiconductor device manufacturing tool of claim 12,wherein the third input is a recycle input from the wet etchingchambers.
 14. The semiconductor device manufacturing tool of claim 8,wherein at least one of the wet etching chambers comprises a rotatablechuck.
 15. A semiconductor device manufacturing tool comprising: a wetetching section comprising a wet etching station; a plasma treatmentsection comprising a plasma treatment station; a transferred stationbetween the wet etching section and the plasma treatment section; and ahousing around the wet etch section, the plasma treatment section, andthe transfer station, wherein the transfer station is configured totransfer a wafer from the wet etching station to the plasma treatmentstation without breaking to exterior atmosphere.
 16. The semiconductordevice manufacturing tool of claim 15, wherein the plasma treatmentsection comprises a chamber housing located inside the housing.
 17. Thesemiconductor device manufacturing tool of claim 16, wherein the plasmatreatment section comprises a mounting platform configured to supportthe wafer, and comprises a first electrode embedded in the mountingplatform, wherein the mounting platform and the first electrode areinside the chamber housing.
 18. The semiconductor device manufacturingtool of claim 17, wherein the plasma treatment section further comprisesa second electrode disposed outside the chamber housing, wherein thefirst electrode and the second electrode are configured to turn a gassource inside the chamber housing into a plasma during plasma treatmentfor the wafer.
 19. The semiconductor device manufacturing tool of claim15, wherein the wet etch section comprises a feed tank configured tofeed an etchant to the wet etching station, wherein the wet etch sectionis configured to reuse used etchant from the wet etching station. 20.The semiconductor device manufacturing tool of claim 19, wherein thefeed tank comprises: a first input coupled to an etchant supply andconfigured to accept a first etchant; a first output coupled to an inputof the wet etching station and configured to supply the first etchant tothe wet etching station; a second input coupled to an output of the wetetching station and configured to accept a used first etchant from thewet etching station; and a third input configured to accept an oxidizerto recover the effectiveness of the used first etchant.